Daneshkazemi A, Davari A, Mousavinasab M, Hatami Hajagha M. Effect of Numbers of Load Cycling on the Micro Tensile Bond Strength of Total Etch Adhesives to Dentin. JSSU 2013; 21 (2) :161-171
URL:
http://jssu.ssu.ac.ir/article-1-2423-en.html
Abstract: (21082 Views)
Introduction: Today load cycling is used for similarity of invitro and invivo studies, though different results were reported in different studies. Therefore, this study aimed to investigate the effect of load cycling on micro tensile bond strength of two total etch adhesives to dentin.
Methods: Enamel of 48 molar teeth were removed to expose the superficial dentin. The teeth were randomly divided into two equal groups, and were restored with Single bond (SB), ExciTE and Synergy composite. Then the teeth of each group were divided to 4 equal sub groups. Moreover, load cycling of 0, 50, 100, 200 k load cycle with 50 newton load was used. In each sub group, 12 hour glass slabs with 1mm2 thickness were made. Then the samples were loaded by Dartec testing machine (Model HC/10) with 1 mm/min cross head speed to make the fracture occur. Data were analyzed by ANOVA, t-test, Bonferroni tests.
Results: The most micro tensile bond strength belonged to ExciTE without load cycling and lowest refered to SB with 200 k. There was a significant difference between the groups (p ExciTE= 0.0001, p SB = 0.001). Micro tensile bond strength in SB group was significantly lower than ExciTE (p= 0.001). Moreover, load cycling had negative effect on micro tensile bond strength.
Conclusion: By increasing load cycling, micro tensile bond strength of both bondings decreased significantly
Type of Study:
Original article |
Subject:
Dental Received: 2013/06/3 | Accepted: 2013/09/28 | Published: 2013/09/28